V-500
Vinyl Ester-Based Chemical Anchor
This is a two-component, styrene-free, high-performance chemical anchor specifically developed for anchoring anchor rods in concrete and for rebar splicing applications.
All Products
General Features
-
It is suitable for structural and non-structural connection anchoring and rebar splicing applications.
-
It can be used in overhead/ceiling applications.
-
It can be used in both cracked and non-cracked concrete.
-
It has ETA-approved performance values according to Seismic Categories C1 and C2.
-
It can be used in anchorage details with short corner and spacing distances.
-
It has an application temperature range from -5°C to +40°C.
-
It does not have a strong odor because it does not contain styrene.
Applications
-
It can be used for securing facade, roof, wood, or metal elements; for installing metal profiles, columns, beams, cantilevers, railings, plumbing fixtures, bathroom fixtures, cable trays, pipes, or reinforcing bars added as post-installed bars for renovation or reinforcement purposes.
-
It is suitable for use in cracked or non-cracked concrete, lightweight concrete, aerated concrete, or natural stone.
-
Since it may cause color changes or discoloration in natural stone, it should be tested prior to application.
-
Anchoring elements: Threaded anchor rods (electro-galvanized or hot-dip galvanized, stainless steel, and high-corrosion-resistant steel), reinforced concrete bars, internally threaded rods, rod profiles, perforated steel sections (e.g., perforated sections),
-
Application temperature: -10°C to +40°C, cartridge temperature: +5°C to +40°C (optimal at +20°C),
-
Service temperature (main material temperature after curing): -40°C to +80°C.
Technical Specifications
Concrete Temperature
-5°F to -1°F
0°F to +4°F
+5°F to +9°F
+10°F to +14°F
+15°F to +19°F
+20°F to +29°F
+30°F to +34°F
+35°F to +40°F
Max. Operating Time
90 min.
45 min.
25 min.
20 min.
15 min.
6 min.
4 min.
2 min.
Minimum Curing Time
6 hours
3 hours
2 hours
100 min.
80 min.
45 min.
25 min.
20 min.